PP Wire Drawing Material Polypropylene T30S/S1003/L5E89

Introducing our high-quality PP wire drawing material: a colorless, tasteless, non-toxic, and odorless thermoplastic polymer. With a neat structure, it is a lightweight and versatile plastic ideal for a variety of applications. Perfect for creating durable and reliable products.

Product Description

Product Listing:

PP T30S is suitable for woven ribbon; used for packaging, carpet backing, artificial turf, bundling rope, packaging rope and other applications; used for film silk, textile film silk, carpet backing.
PP S1003 is suitable for narrow band and flat wire.
PP L5E89 is suitable for making textile fibers, woven bags, carpet backing, sand distribution, strapping materials, ropes, etc.

PP T30S
Physical properties	Test Method	Value	Unit
Density	ISO1183	0.905	g/cm3
Melt Flow Rate	ISO1133	3.5	g/10min
Rockwell Hardness	ISO2039-2	95
MechanicalPropertes
Tensile Strength	ISO527-2		MPa
Flexural Modulus	ISO178		MPa
Elongation at Break	——	——	——
Charpy Notched Impact Strength	ISQ179-1	3	KI/m2
ThermalProperties
Heat Deflection Temperature	ISO75-2	105	℃
Vicat Softening Point	——	——	——

PP S1003
Physical properties	Test Method	Value	Unit
IZOD notch impact strength	ASTMD-256	13	kg.cm/cm
IZOD notch impact strength	ASTMD-256	45	kg.cm/cm
Stiffness coefficient	ASTM D-790	11200	kg/cm
Rockwell hardness	ASTMD-785	95	R Ruler
Tensile strength at yield point	ASTM D-638	250	kg/cm
Shrinkage	ASTM D-638	450	%
Shrinkage	YCCI	0.5-1.7	%
Aging resistance	ASTMD-3045	>500	Hours
Combustibility	UL94	HB	Grade
Thermal deformation temperature	ASTMD-648	110	℃
Weatherability	ASTMD-1499	180	Hours
Density/Specific Gravity	ASTM D-792	0.9	g/cm
Melt index	ASTMD-1238	2	g/10min

PP L5E89
Physical properties	Test Method	Value	Unit
Color Granules	SHT 1541	≤5	Pieces/kg
Black Granules	SH/T 1541	0	Pieces/kg
Big & Small Granules	SH/T 1541	≤20	g/kg
MFR	GB/T 3682	3.5±0.5	g/10min
Isotactic Index	GB/T 2412	≥180	%
Ash Content	GB/T 9345.1	≤300	mg/kg
Tensile Yield Stress	GB/T 1040.2	≥31	MPa
Tensile Fracture Stress	GB/T 1040.2	≥16	MPa
Tensile Fracture Nominal Strain	GB/T 1040.2	≥180	%
Yellow Index	HG/T 3862	≤4.0	Hours

Applications

PP T30S is suitable for woven ribbon; used for packaging, carpet backing, artificial turf, bundling rope, packaging rope and other applications; used for film silk, textile film silk, carpet backing.

PP S1003 is suitable for narrow band and flat wire.

PP L5E89 is suitable for making textile fibers, woven bags, carpet backing, sand distribution, strapping materials, ropes, etc.

PP Wire Drawing Material Polypropylene T30S/S1003/L5E89